KIMYA - PETG Carbon Filament
KIMYA PETG Carbon Filament The Kimya PETG Carbon 3D filament is a mixture of PETG and carbon fibers. The addition of carbon fibers to PETG provides high levels of mechanical performance. Thanks to its rigidity, the PETG Carbon is highly valued in the production of special parts, notably in the paramedical and automotive fields. The Kimya PETG Carbon 3D filament has the following properties: High rigidity Improve ratio between: Ease of printing / Rigidity Complies with the REACH standard Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg FILAMENT PROPERTIES PROPERTIES TEST METHODS VALUES Density ISO 1183-1 1.28 g/cm3 Moisture rate INS-6711 < 10 % Melt flow index (MFI) ISO 1133-1 (@225°C – 2.16 kg) 9.7 g/10min Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-300°C) 76 °C PRINT PARAMETERS AND SPECIMENS DIMENSIONS PRINTING DIRECTION XY Printing Speed 40-70 mm/s Infill 100% - rectilinear
KIMYA PETG Carbon Filament
The Kimya PETG Carbon 3D filament is a mixture of PETG and carbon fibers. The addition of carbon fibers to PETG provides high levels of mechanical performance. Thanks to its rigidity, the PETG Carbon is highly valued in the production of special parts, notably in the paramedical and automotive fields. The Kimya PETG Carbon 3D filament has the following properties:
High rigidity
Improve ratio between: Ease of printing / Rigidity
Complies with the REACH standard
Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg
FILAMENT PROPERTIES
PROPERTIES
TEST METHODS
VALUES
Density
ISO 1183-1
1.28 g/cm3
Moisture rate
INS-6711
< 10 %
Melt flow index (MFI)
ISO 1133-1 (@225°C – 2.16 kg)
9.7 g/10min
Glass transition temperature (Tg)
ISO 11357-1 DSC (10°C/min - 20-300°C)
76 °C
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION
XY
Printing Speed
40-70 mm/s
Infill
100% - rectilinear
Infill Angle
45°/-45°
Nozzle Temperature
220-260°C
Bed T°
60-100°C
PRINTED SPECIMENS PROPERTIES
PROPERTIES
TEST METHODS
VALUES
MECHANICAL PROPERTIES
Tensile modulus
ISO 527-2/5A/50
4,541 MPa
Tensile Strength
ISO 527-2/5A/50
52.9 MPa
Tensile strain at strength
ISO 527-2/5A/50
2.4 %
Tensile Stress at Break
ISO 527-2/5A/50
41.3 MPa
Tensile strain at break
ISO 527-2/5A/50
2.6 %
Flexural modulus
ISO 178
2,648 MPa
Flexural stress at conventional deflection (3,5% strain)*
ISO 178
80.4 MPa
Flexural stress at break
ISO 178
80 MPa
Charpy impact resistance
ISO 179-1/1eA
4.1 kJ/m²
Shore Hardness
ISO 868
75D
Note 1
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2
The data should be considered as indicative values - Properties can be influenced by production conditions.
MakerBot Method Labs ABS Carbon Filament (.5kg, 1.1lb)
XYZprinting Carbon Fibre (600 g) - Black - 3D filament - LDLC
Kimya PETG Carbon get3D - drukarki 3D, akcesoria i filamenty
KIMYA PT1024TQ: PETG-S filament, black, 1.75 mm, 4500 g at reichelt elektronik
AON3D ReadyPrint™ PETG Filament, Black, 1.75mm, 2kg Powered by Kimya
Kimya PETG Carbon Black, 1.75mm
Kimya PETG-S (2.85mm, 750g)
KIMYA publishes the results of a life cycle analysis of its recycled PETG filaments - 3DPC
3DGBIRE Appointed Distributor of Kimya Filaments
KIMYA Tough Bundle (2.85mm)
siraya tech resin
KIMYA - PETG Carbon Filament
Kimya PETG Carbon Black - fbrc8 llc
Filament PETG-S Kimya pour vos impression 3D